Polyester T80 asosidagi quyma poliuretan prepolimer

HJ-3875

HJ-3880

HJ-3885

HJ-3890

NCO foiz tarkibi

2.6±0.2

3.0±0.2

3.5±0.2

4.3±0.2

Zichlik25 degree /(g/cm³)

1.23

1.23

1.23

1.23

Yopishqoqlik80 degree /mpa·s

1800-2200

1700-2100

1500-1800

1200-1600

Ko'rinish 25daraja

Oq qattiq

Aralash haroratidaraja

Prepolimer/Moca

85 daraja / 115 daraja

85 daraja / 115 daraja

85 daraja / 115 daraja

80 daraja / 115 daraja

Jel vaqti/min

8-10

4-7

4-7

2-4

Vulkanizatsiya vaqti (h)

25-16

25-16

25-16

25-16

Jismoniy xususiyatlar

Qattiqlik (Shore A)

75±2

80±2

85±2

90±2

Kuchlanish kuchi (Mpa)

30-37

38-45

42-48

45-50

100 foiz modul (Mpa)

9-10

9-10

10-11

10-12

300 foiz modul (Mpa)

14-15

14-15

15-17

17-20

Tanaffusdagi cho'zilish (foiz)

650-720

630-700

610-680

600-660

Yirtilish kuchi (KN/m)

60-70

75-82

82-95

100-115

Siqilishning doimiy deformatsiyasi foizi

6-8

8-10

6-10

8-10

DIN Aşınma yo'qolishi（mm³）

55 dan kam yoki teng

50 dan kam yoki teng

48 dan kichik yoki teng

45 dan kam yoki teng

Chidamlilik foizi /25daraja

24-26

23-25

20-23

18-22

Mahsulot qoʻllanilishi: Rod va bar, varaq va plastinka, gʻaltak, tortuvchi rolik, tasniflash ekrani, mufta, moy{0}}quvur tozalagich, muhrlash halqasi, siklon, qirgʻich va boshqa mahsulotlar.

Operatsiya tafsilotlari:

80-85 daraja vakuumli degazatsiyadan so'ng, prepolimer quyma va vulkanizatsiya uchun eritilgan MOCA bilan aralashtiriladi. Bu qo'lda va mexanik ishlov berish uchun javob beradi.

Saqlash:

Salqin va quruq joyda saqlang va ochilgandan keyin iloji boricha tezroq foydalaning; Agar uni bir vaqtning o'zida ishlatish mumkin bo'lmasa, u azot bilan yopishtirilishi kerak; Ikkinchi ochilishni ko'pikni yo'qotish uchun ishlatish kerak va asl saqlash muddati olti oy.

Qadoqlash:

20kg yoki 200kggiron baraban

HJ-3832

HJ-3842

HJ-3893

HJ-3895

NCO foiz tarkibi

3.2±0.2

4.2±0.2

4.7±0.2

5.0±0.2

Zichlik25 degree /(g/cm³)

1.23

1.23

1.23

1.23

Yopishqoqlik80 degree /mpa·s

1600-1800

1500-1700

1000-1200

900-1100

Ko'rinish 25daraja

Oq qattiq

Aralash haroratidaraja

Prepolimer/Moca

85 daraja / 115 daraja

80 daraja / 115 daraja

80 daraja / 115 daraja

75 daraja / 115 daraja

Jel vaqti/min

4-6

3-5

2-3

2-3

Vulkanizatsiya vaqti (h)

25-16

25-16

25-16

25-16

Jismoniy xususiyatlar

Qattiqlik (Shore A)

82±2

90±2

93±2

95±2

Kuchlanish kuchi (Mpa)

38-43

40-45

45-49

45-50

100 foiz modul (Mpa)

10-11

10-12

8-10

8-10

300 foiz modul (Mpa)

14-15

15-16

16-18

16-18

Tanaffusdagi cho'zilish (foiz)

650-750

580-700

570-680

550-680

Yirtilish kuchi (KN/m)

80-90

85-95

110-130

115-135

Siqilishning doimiy deformatsiyasi foizi

4-6

4-6

2-4

2-4

DIN Aşınma yo'qolishi（mm³）

55 dan kam yoki teng

50 dan kam yoki teng

45 dan kam yoki teng

45 dan kam yoki teng

Chidamlilik foizi /25daraja

22-25

20-23

18-22

16-18

Mahsulotni qoʻllash sohasi: novda va novda, lavha va plastinka, gʻaltak, tortuvchi rolik, tasniflash ekrani, mufta, moy{0}}quvur tozalagich, muhrlash halqasi, siklon, qirgʻich va boshqa mahsulotlar.

Operatsiya tafsilotlari:

80-85 daraja vakuumli degazatsiyadan so'ng, prepolimer quyma va vulkanizatsiya uchun eritilgan MOCA bilan aralashtiriladi. Bu qo'lda va mexanik ishlov berish uchun javob beradi.

Saqlash:

Salqin va quruq joyda saqlang va ochilgandan keyin iloji boricha tezroq foydalaning; Agar uni bir vaqtning o'zida ishlatish mumkin bo'lmasa, u azot bilan yopishtirilishi kerak; Ikkinchi ochilishni ko'pikni yo'qotish uchun ishlatish kerak va asl saqlash muddati olti oy.

Qadoqlash:

20kg yoki 200kggiron baraban